16CRMO44/ DIN 1.7337 QUALITY ALLOY STEEL

16CrMo44/DIN 1.7337 steel  is a low-alloy steel containing chromium and molybdenum as strengthening elements.Similar to the Chinese grade 15CrMo,16CrMo44 steel has good process performance and welding performance, and has a high lasting strength at a temperature of 500 to 550 °C.Once the temperature exceeds 550 °C, its oxidation resistance becomes poor, and the creep strength decreases significantly.

16CrMo44 steel is generally used in the quenched and tempered condition.It is used to manufacture high and medium pressure steam conduits, headers, superheaters and supporting forgings.

16CRMO44/ DIN 1.7337 QUALITY ALLOY STEEL

Chemical Composition

Grade C Si Mn P S Cr Mo
16CrMo44 0.13-0.2 0.15-0.35 0.5-0.8 ≤0.025 ≤0.035 0.9-1.2 0.4-0.5
15CrMo 0.12-0.18 0.17-0.37 0.4-0.7 ≤0.035 ≤0.035 0.8-1.1 0.4-0.55

Heat Treatment
Normalizing For 16CrMo44
1.Nominal normalizing temperature:840-890°C
2.Hold the temperature for several hours
3.Cooling in the air

Annealing  For 16CrMo44
1.Nominal Annealing temperature:680-720°C
2.Cool slowly in the furance
3.Maximum Brinell hardness of 217

Quenching and Tempering(QT)  For 16CrMo44
1.Nominal Hardening temperature:890-920°C
2.Hold at this temperature then quench in oil or water
3.Tempering  as soon as possible when the temperature low to ambient
4.Heat uniformly to the suitable temperature of 650-720°C
5.keep the material out of the furnace ,then cool in the air

16CrMo44 Mechanical Property in Q&T condition

Tensile Strength Mpa Yield Strength Mpa Elongation % Reduction of Area % Impact Charpy-V,J
 ≥440   ≥295  ≥22   ≥60  ≥94

Quality Certification
A material test report(Inspection Certificate EN 10204 3.1) will be provided, documenting the following:
1.Chemical analysis
2.Mechanical properties
3.Surface hardness
4.Non Metallic Inclusion
5.Heat Treatment Process
6.Grain size
7.Forging ratio
8.NDE test method/criteria

16CrMo44 Supply Form & Size

  • Round Bars:  Dia.80 – 1,000mm as Forged
  • Flat / Square Bars:  Thickness Max.800mm
  • Shafts, Rollers, Blocks,Tubes:  Customized or According to Drawing
  • Rolled Round Bars:  Dia.16 – 130mm with UT Assurance

Heat treatment: Normalizing (+N), Annealing (+A),Q&T
Surface finish:Black / Rough turned / Peeled

16CrMo44/1.7337 alloy steel manufacturers and suppliers,supplied with round rods,square/flat bars,rollers,shafts,blocks and forging pieces.